Sell Double components Fireproofing architectural silicone sealant

1)architectural silicon sealantmanufacturer
2)High bond strength,
3)Acid and alkali resistance
4)Double-components

 Double Components Structural architectural silicone sealant 

Description

FJ-9900 Silicone insulating glass sealant is a two-parts, neutral curing silicone sealant specifically developed for the manufacture of high performance insulated glass with good features as follows:

a. Insulating glass manufactured by FJ-9900 conforms to GB/T11944

b. Excellent adhesion to all kinds of glass

c. Neutral cured, no corrosion, non poisonous

d. Excellent structural strength with temperature durable performance at 50°C~+150°C 

e. Excellent weatherproof and UV, high temperature and humidity stability.

No limitation for batch time match

 

Where to use

1. It is formulated for making the secondary seal in a dual sealed insulating glass unit.

2. The high performance features incorporated into this product make it especially suitable for the following applications:

1) Insulated glass unit for commercial buildings

2) Insulated glass unit incorporating specialty glass types, or with free edges (solar architecture).

3) Insulated glass unit where high heat or humidity maybe encountered.

 

l Technical index (for reference)

The following data is for reference, is not suggested to make standard.

  

Item	Base	Curing Agent	Mixed Base to Curing Agent by Volume	Test method
Colors	White	Black	Black, no flow paste
Specific gravity	1.38	1.02	1.33
Shelf life, month	12	12
Mixed at 12:1 Base to Curing Agent by weight (or 9:1 by volume)
Working Time((humidity 50±5%,temperature 23±2°C)		minutes	20-40
Tack free time (humidity 50±5%,temperature 23±2°C)		minutes	80-100
Corrosive			no
As Cured  7 Days at (humidity 50±5%,temperature 23±2°C)
Ultimate tensile strength		MPa	0.85	GB/T113477
Ultimate elongation		%	120	GB/T113477
Hardness (Shore A)			42	GB/T1531
Service temperature range		°C	50°C~+150°C ( -58~+302F)