Supply Flame Retardantmaterial PPS Plastics

Click image to view original picture
Product/Service: Flame Retardantmaterial PPS Plastics  
Unit Price: Negotiating  Inquiry
The min order:  
Total Supply:
Delivery Expiry: Delivery within 3 days after payment from buyer
Validity Period: Longterm Validity
Last Update: 2012-04-12
Browse: 1382
Basic Info of Company
 
 
Product detailed description

PPS Excellent chemical resistance
PPS tight tolerance
PPS better thermal performance
PPS-dimensional stable flame retardant

Property 

Test Method

Units

Fiberglass Reinforced

P130T

P130T-04

P140T

P140T-02

P140T-04

Physical

Density

ISO 1183

g/cm3

1.56

1.56

1.65

1.65

1.65

Water Absorption

ISO 62

%

0.02

0.02

0.02

0.02

0.02

MD/TD*

 -

%

0.4/0.7

0.4/0.7

0.3/0.6

0.3/0.6

0.3/0.6

Mechanical

Tensile Strength

ISO 527

MPa

150

145

185

180

175

Elongation at Break

ISO 527

%

3.0

6.0

2.0

4.0

4.0

Flexural Strength

ISO 178

MPa

220

210

260

250

250

Flexural Modulus

ISO 178

GPa

11.0

8.0

13.0

12.0

11.5

Impact Strength

ISO 180

kJ/m2

10.0

12.0

12.0

14.0

15.0

Rockwell Hardness

ISO 2039/2

R scale

120

120

120

120

120

Thermal

Heat Deflection Temperature

ISO 75

°C

265

265

265

265

265

Flammability Rating

UL-94

-

V0

V0

V0

V0

V0

Electrical

Volume Resistivity

ISO 167

Ohm.cm

5×1016

5×1016

5×1016

5×1016

5×1016

Dielectric Strength

ASTM D149

KV/mm

16

16

16

16

16

Dielectric Constant

ASTM D150

-

3.6

3.6

3.8

3.8

3.8

Wastage Factor

ASTM D150

-

0.002

0.002

0.002

0.002

0.002

Process

Conditions

Injection Temperature

-

°C

290~330

290~330

290~330

290~330

290~330

Mold Temperature

-

°C

120~150

120~150

120~150

120~150

120~150

* MD: Mold direction; TD: Transverse direction

 