ZB60-1 Outdoor Thick Film Steel Structure Heat Insulation fireproof Coating
Product de
|
Ø Inorganic bond and multiple insulating refractory based with water as dispersion medium. Epoxy paint. Ø Excellent anti-fire and anti-hot capability, enduring long time high-temperature fire concussion. Ø Great cohesional strength, impermeability,strong adhesion force, high pressive strength Ø Good resistance of climatehumidity Ø Freeze proof, no crusting, no spalling, no aging Ø long term usage. |
Recommended uses
---Anti-fire protection of steel structure (inside and outside) in petrochemical industry enterprise
---Anti-fire protection of large-scale highway, railway and tunnel etc.
|
Capability of anti-fire |
||||||
|
Thickness of coat anti-fire of common construction |
Fire resistance limit(h) |
1.0 |
1.5 |
2.0 |
2.5 |
3.0 |
|
Coat thickness(mm) |
8.3 |
12.4 |
16.6 |
20.7 |
24.8 |
|
|
Thickness of coat anti-fire of hydrocarbon |
Fire resistance limit(h) |
1.0 |
1.5 |
2.0 |
2.5 |
3.0 |
|
Coat thickness(mm) |
13.3 |
17.4 |
21.6 |
25.7 |
29.8 |
|
|
Theory dosage: the using area of coat (per ton) in different thickness |
||||||
|
Coat thickness (mm) |
10 |
15 |
20 |
25 |
30 |
35 |
|
Coat area (m2) |
150 |
100 |
75 |
60 |
50 |
42 |
|
Technical items: (indoor) |
|
|
Test item |
Technical target |
|
1. State in the container |
Liquid in symmetrical and thickness without agglomeration after stirring |
|
2. Desiccation time(surface dry) |
≤5 hours |
|
3. Appearance and color |
offwhite |
|
4. Crack resistance of earlier drying |
Pass muster |
|
5. Cohesional strength |
≥0.04(Mpa) |
|
6. Pressive strength |
≥0.3(Mpa) |
|
7. Dry density (kg/) |
≤500 |
|
8. Water resisting property (h) |
24 without spilly space, sudsing, drop off |
|
9. Hot and cold circulation resistant(times) |
15 without cracking, spalling, sudsing |
|
Technical items: (Outdoors) |
|
|
Test item |
Technical target |
|
1. State in the container |
Liquid in symmetrical and thickness without agglomeration after stirring |
|
2. Desiccation time(surface dry) |
≤5 hours |
|
3. Appearance and color |
offwhite |
|
4. Crack resistance of earlier drying |
Pass muster |
|
5. Cohesional strength |
≥0.04 |
|
6. Pressive strength |
≥0.5 |
|
7. Dry density (kg/) |
≤650 |
|
8. Exposure hot resistant (h) |
≥720 without spilly space, drop off, cracking |
|
9. Resistance to heat and humidity (h) |
≥504 without spilly space, drop off |
|
10. Freezing and thawing cycle resistant (times) |
≥15 without cracking, spalling, sudsing |
|
11. Acid resistant (h) |
≥360 without cracking, spalling,spilly space |
|
12. Alkali resistant (h) |
≥360 without cracking, spalling, spilly space |
|
13. Salt fog resistance (times) |
≥30 without sudsing, obvious metamorphism, intenerating |
Attention
The paint is single component. Mixing around and using the paint wholly for one time.
Maintain for 28 days when painting to the designed thickness to reach the due strength.
Storage period
Best storage period: 3 months. Time extend will reduce the cohesional strength.
epoxy paint, fireproof coating, protective coatings