1.fire clay bricks for blast furnances
2. high-tempreture resistace
3. good eroding resistance
4.used in cement factory
Chinese Refractory raw material resources are abundant, which are suitable for the production of various grades of insulating firebrick. Limiting temperature of use range from 900º C to 1650º C. Each grade of insulating firebrick is formulated to meet specific thermal and physical requirements. Top grade insulating firebrick are made from high-purity refractory clays, with graduated additions of alumina for the higher temperature products, and a carefully graded organic filler, which burns out during manufacture to give a controlled, uniform lacuna structure. Each brick machined to precise size on all six faces. The maximum continue use temperature depends on application. If you have any question, please feel free to contact us.
A: high alumina brick
Item | LZ-75 | LZ-65 | LZ-55 | LZ-48 | |
Al2O3,% min | 75 | 65 | 55 | 48 | |
Refractoriness min | 1790 | 1790 | 1770 | 1750 | |
RUL min | 1520 | 1500 | 1470 | 1420 | |
P.L.C.1500ºC X 2h | 0.1-0.4 1500ºC X 2h | 0-0.2 | |||
A.P.max | 23 | 23 | 22 | 22 | |
CCS; max | 53.9 | 49.0 | 44.1 | 39.2 |
B: clay brick
Target |
Grades and numerical |
||
(NZ)-42 |
(NZ)-40 |
(NZ)-38 |
|
Al2O3 content not below |
42 |
40 |
38 |
Refractoriness °C not below |
1750 |
1730 |
1690 |
2Kg/cm2 load softening temperature °C start not less than |
1400 |
1350 |
1300 |
Refiring linear contractive % °C 1450 2 hours is not more than |
+0.1 |
||
Refiring linear contractive % 1350 °C 2 hours is not more than |
0.3 |
-0.5 |
|
Show porosity % |
22 |
24 |
26 |
Kgfcm2 not less than the normal temperature compression strength |
250 |
200 |
150 |